Research PaperExtraction of alumina from KAOLIN (cas 1332-58-7) by a combination of pyro- and hydro-metallurgical processes
-
Add time:08/25/2019 Source:sciencedirect.com
The increasing of aluminum demand globally raises the interest in developing alternative technologies to produce alumina from non-bauxitic sources, especially clays. This paper studies the extraction of alumina from the KAOLIN (cas 1332-58-7) ore excavated from the Irkutsk region, Russia through the leaching process, using aqueous solutions of sodium carbonate as a leaching agent. Before the leaching process, the kaolin ore and limestone charge was sintered. The sintering process achieves the dehydroxylation of the kaolinite, which is the main mineralogical phase in the kaolin and activates its transformation to metakaolin. Metakaolin is an amorphous AlSi phase, from which alumina could be easily leached. The annealed sintered material transform into dust that is suitable for the leaching process without any additional grinding. The sintering process was taken place in the temperature range 800-1400 °C for 1 h. The effect of briquetting pressure and sintering temperature on the recovery of alumina from kaolin, were studied. About 87% of the alumina in the kaolin was extracted at 1360 °C and briquetting pressure of 5 MPa.
We also recommend Trading Suppliers and Manufacturers of KAOLIN (cas 1332-58-7). Pls Click Website Link as below: cas 1332-58-7 suppliers
Prev:Original ArticlePreparation of glass-ceramic materials using KAOLIN (cas 1332-58-7) and oil well drilling wastes
Next:Effect of curing temperature and relative humidity on the hydrates and porosity of calcium sulfoaluminate cement) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Original ArticlePreparation of glass-ceramic materials using KAOLIN (cas 1332-58-7) and oil well drilling wastes08/24/2019
- Research paperInsights on the clay reactivity in alkaline media: Beyond filler role for KAOLIN (cas 1332-58-7)08/23/2019
- Original ArticleInfluence of an aging step on the synthesis of zeolite NaA from Brazilian Amazon KAOLIN (cas 1332-58-7) waste08/22/2019
- Metallogenic process of ion adsorption REE ore based on the occurrence regularity of La in KAOLIN (cas 1332-58-7)08/21/2019
- Effect of KAOLIN (cas 1332-58-7) content on the performances of KAOLIN (cas 1332-58-7)-hybridized soybean meal-based adhesives for wood composites08/20/2019
- 2D KAOLIN (cas 1332-58-7) ultrafiltration membrane with ultrahigh flux for water purification08/19/2019
- Cleaning and upgrading of coal-series KAOLIN (cas 1332-58-7) fines via decarbonization using triboelectric separation08/18/2019
- Effect of KAOLIN (cas 1332-58-7) content and sonication on the properties of wheat gluten composites08/17/2019