Electrochromic properties of Rhodium oxide (cas 12036-35-0) thin films prepared by reactive sputtering under an O2 or H2O vapor atmosphere
-
Add time:07/27/2019 Source:sciencedirect.com
Rhodium (Rh) oxide thin films were prepared by reactive sputtering at different substrate temperatures under an oxygen or water (H2O) vapor atmosphere, and their crystal structure, density, optical properties, and electrochromic properties were investigated. The film density decreased with decreasing substrate temperature, and the lowest density of 4.2 g/cm3 was obtained for the film deposited at −20 °C under a H2O vapor atmosphere. The Rh oxide films deposited at −20 °C under a H2O vapor atmosphere showed anodic electrochromism between light yellow and olive i.e., bleached and colored states, respectively using an aqueous 1 M potassium hydroxide as the electrolyte; these films also exhibited the largest transmittance change, of 26%, at a wavelength of 600 nm.
We also recommend Trading Suppliers and Manufacturers of Rhodium oxide (cas 12036-35-0). Pls Click Website Link as below: cas 12036-35-0 suppliers
Prev:Microstructure and oxidation performance of undoped and rhodium-doped aluminide coatings on Mar-M247 superalloy
Next:Synthesis, characterization and hydrogen sensing properties of nanosized colloidal Rhodium oxide (cas 12036-35-0)s prepared by Pulsed Laser Ablation in water) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Decorating cobalt phosphide and rhodium on reduced graphene oxide for high-efficiency hydrogen evolution reaction07/29/2019
- Synthesis, characterization and hydrogen sensing properties of nanosized colloidal Rhodium oxide (cas 12036-35-0)s prepared by Pulsed Laser Ablation in water07/28/2019
- Microstructure and oxidation performance of undoped and rhodium-doped aluminide coatings on Mar-M247 superalloy07/26/2019
-
Health and Chemical more >